The new ternary silicide Gd5CoSi2: Structural, magnetic and magnetocaloric properties

Résumé

Gd5CoSi2 was prepared by annealing at 1003 K. Its investigation by the X-ray powder diffraction shows that the ternary silicide crystallizes in a tetragonal structure deriving from the Cr5B3-type (I4/mcm space group; a=7.5799(4) and c=13.5091(12) Å as unit cell parameters). The Rietveld refinement shows a mixed occupancy on the (8h) site between Si and Co atoms. Magnetization and specific heat measurements performed on Gd5CoSi2 reveal a ferromagnetic behaviour below TC=168 K. This magnetic ordering is associated to an interesting magnetocaloric effect; the adiabatic temperature change ΔTad is about 3.1 and 5.9 K, respectively, for a magnetic field change of 2 and 4.6 T.

Domaines

Matériaux
Fichier principal
Vignette du fichier
11013.pdf (823.65 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-00565319 , version 1 (11-02-2011)

Identifiants

Citer

Charlotte Mayer, Etienne Gaudin, Stéphane Gorsse, Bernard Chevalier. The new ternary silicide Gd5CoSi2: Structural, magnetic and magnetocaloric properties. Journal of Solid State Chemistry, 2011, 184 (2), pp.325-330. ⟨10.1016/j.jssc.2010.11.023⟩. ⟨hal-00565319⟩
138 Consultations
219 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More