Quantification of boron coordination changes between lithium borate glasses and melts by neutron diffraction - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Physics and Chemistry of Glasses Année : 2009

Quantification of boron coordination changes between lithium borate glasses and melts by neutron diffraction

Résumé

The structure of lithium borate glasses and liquids (xLi2O.(1−x)B2O3, with x=0·1, 0·20, 0·25 and 0·33) has been investigated by neutron diffraction coupled with Li isotopic substitution at temperatures up to 1173–1273 K. Both the short range order around B and Li is changed, with the conversion of BO4 to BO3 and a subsequent increase of NBOs (nonbridging oxygens) around Li as temperature increases. The quantitative boron coordination change has been assessed by a Gaussian fitting of the B–O pair contribution. The increasing presence of NBOs results in the opening of the borate network and the disappearance of superstructural borate rings. The reorganisation of the structure above the glass transition temperature provides a structural mechanism for the modifications of the thermodynamic and configurational properties of borate liquids.
Fichier non déposé

Dates et versions

hal-00492551 , version 1 (16-06-2010)

Identifiants

  • HAL Id : hal-00492551 , version 1

Citer

Laurent Cormier, Georges Calas, Brigitte Beuneu. Quantification of boron coordination changes between lithium borate glasses and melts by neutron diffraction. Physics and Chemistry of Glasses, 2009, 50 (3), pp.195-200. ⟨hal-00492551⟩
279 Consultations
0 Téléchargements

Partager

Gmail Facebook X LinkedIn More