Polystyrene grafting from silica nanoparticles via Nitroxide-Mediated-Polymerization (NMP): synthesis and SANS analysis with contrast variation method, - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Soft Matter Année : 2009

Polystyrene grafting from silica nanoparticles via Nitroxide-Mediated-Polymerization (NMP): synthesis and SANS analysis with contrast variation method,

Chloé Chevigny
Didier Gigmes
Denis Bertin
François Boué

Résumé

We present a new convenient and efficient “grafting from” method to obtain well defined polystyrene (PS) silica nanoparticles. The method, based on Nitroxide-Mediated Polymerization (NMP), consists to bind covalently the alkoxyamine, which acts as initiator controller agent, at the silica nanoparticles surface in two steps. The first step is a reaction between the aminopropylsilane and the silica particles in order to functionalize the particles surface with amino group. In a second step, the initiating-controlling alkoxyamine moiety is introduced via an over grafting reaction between the amino group and the N-hydroxysuccinimide based MAMA-SG1 activated ester. To simplify both their chemical transformation and the polymerization step, the native silica particles, initially dispersed in water, have been transferred in an organic solvent, the dimethylacetamide, which is also a good solvent for the polystyrene. The synthesis parameters have been optimized for grafting density, conversion rates, and synthesis reproducibility while keeping the colloidal stability and to avoid any aggregation of silica particles induced by the inter-particles interaction evolution during the synthesis. After synthesis, the final grafted objects have been purified and the non-grafted polymer chains formed in the solvent have been washed out by ultra filtration. Then the particles have been studied using Small angle Neutron Scattering (SANS) coupled to neutron contrast variation method. To optimize the contrast conditions, both hydrogenated and deuterated monomers have been used for the synthesis. A refined fitting analysis based on the comparison on two models, a basic core-shell and the Gaussian Pedersen model, enables us to fit nicely the experimental data for both the hydrogenated and deuterated grafted case. Differences are seen between grafting of normal or deuterated chains which can be due to monomer reactivity or to neutron contrast effect variations. The synthesis and the characterization method established in this work constitute a robust and reproducible way to design well defined grafted polymer nanoparticles. These objects will be incorporated in polymer matrices in a further step to create Nanocomposites for polymer reinforcement.
Fichier principal
Vignette du fichier
chevigny_soft_matter_2009_hal.pdf (462.74 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00482112 , version 1 (08-05-2010)

Licence

Paternité - Partage selon les Conditions Initiales

Identifiants

Citer

Chloé Chevigny, Didier Gigmes, Denis Bertin, Jacques Jestin, François Boué. Polystyrene grafting from silica nanoparticles via Nitroxide-Mediated-Polymerization (NMP): synthesis and SANS analysis with contrast variation method,. Soft Matter, 2009, 5 (19), pp.3741-3753. ⟨10.1039/b906754j⟩. ⟨hal-00482112⟩
153 Consultations
232 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More