In Situ study of Nucleation of Zirconia in an MgO–Al2O3–SiO2 Glass

Résumé

Crystalline nucleation is investigated during the dynamical heat treatment of a ZrO2–MgO–Al2O3–SiO2 glass by high-temper- ature Zr K-edge X-ray absorption near-edge spectroscopy. In the parent glass, the Zr coordination number is higher than in most glasses, explaining the structural instability of Zr during thermal treatment. The Zr local structure is modified at 301C above the nucleation onset. Crystalline nucleation is characterized by the formation of peculiar nano-ZrO2 particles, which are stable until completion of the thermal treatment. These nano-ZrO2 particles are stable during the elaboration of glass–ceramics, without any Zr41 remaining in the glassy matrix of the final material. i

Dates et versions

hal-00481406 , version 1 (06-05-2010)

Identifiants

Citer

Olivier Dargaud, Georges Calas, Laurent Cormier, Laurence Galoisy, Cecile Jousseaume, et al.. In Situ study of Nucleation of Zirconia in an MgO–Al2O3–SiO2 Glass. Journal of the American Ceramic Society, 2010, 93 (2), pp.342-344. ⟨10.1111/j.1551-2916.2009.03409.x⟩. ⟨hal-00481406⟩
223 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More