Herstellung von dünnen und dichten partiell Yttrium-dotierten Zirkondioxid-Elektrolyten für Brennstoffzellen (IT-SOFC) durch das SPS-Verfahren - Archive ouverte HAL
Article Dans Une Revue Thermal Spray Bulletin Année : 2008

Herstellung von dünnen und dichten partiell Yttrium-dotierten Zirkondioxid-Elektrolyten für Brennstoffzellen (IT-SOFC) durch das SPS-Verfahren

Résumé

Intermediate temperature - solid oxy-fuel cells (IT-SOFCs) include in their design a solid electrolyte layer made of yttria-partially stabilized zirconia (Y-PSZ), an ionic conductor, through which oxygen ions diffuse. This layer needs to fulfill several characteristics among which a low leakage rate corresponding to a non-connected pore network and a low level of stacking defects such as microcracks or globular pores. Moreover, the thickness of this layer needs to be as low as possible (about 20 μm) in order to limit ohmic losses. Suspension plasma spraying (SPS) appears as a potential technological route to manufacture such layers structured at micrometric or sub-micrometric scales. In SPS, a stabilized suspension, made of a liquid solvent, solid particles and a dispersant, is injected within the plasma flow. The liquid is very quickly fragmented and then vaporized and the individual particles, or the particle agglomerates, depending on the average size and morphology of the solid feedstock, are heated and simultaneously accelerated towards the substrate surface where they impact, spread and solidify, analogously in a first approximation to larger particles, to form a layer. The architecture of the layer is very closely related to plasma operating parameters (from which derive plasma flow stability), from the suspension characteristics, in particular the feedstock particle size distribution and from the suspension injection parameters. This work aims at presenting recent developments made to optimize some of these operating parameters to maximize the electrolyte layer characteristics.
Fichier non déposé

Dates et versions

hal-00376899 , version 1 (20-04-2009)

Identifiants

  • HAL Id : hal-00376899 , version 1

Citer

E. Brousse, Alain Denoirjean, Ghislain Montavon, Hélène Ageorges, Vincent Rat, et al.. Herstellung von dünnen und dichten partiell Yttrium-dotierten Zirkondioxid-Elektrolyten für Brennstoffzellen (IT-SOFC) durch das SPS-Verfahren. Thermal Spray Bulletin, 2008, 1, pp.140-147. ⟨hal-00376899⟩

Partager

More