Precipitate stability and recrystallisation in the weld nuggets of friction stir welded Al-Mg-Si and Al-Mg-Sc alloys. - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Science and Engineering: A Année : 2008

Precipitate stability and recrystallisation in the weld nuggets of friction stir welded Al-Mg-Si and Al-Mg-Sc alloys.

Résumé

Two different precipitate hardening aluminium alloys processed by friction stir welding were investigated. The microstructure and the hardness of the as delivered materials were compared to that of the weld nugget. Transmission electron microscopy observations combined with three-dimensional atom probe analyses clearly show that β'' precipitates dissolved in the nugget of the Al-Mg-Si giving rise to some supersaturated solid solution. It is shown that the dramatic softening of the weld could be partly recovered by post-welding ageing treatments. In the Al-Mg-Sc alloy, Al3Sc precipitate size and density are unchanged in the nugget comparing to the base metal. These precipitates strongly reduce the boundary mobility of recrystallised grains, leading to a grain size in the nugget much smaller than in the Al-Mg-Si alloy. Both coherent and incoherent precipitates were detected. This feature may indicate that a combination of continuous and discontinuous recrystallisation occurred in the weld nugget.
Fichier principal
Vignette du fichier
fsw_almgsi_almgsc_sauvage_MSE_08-HAL.pdf (2.63 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00314076 , version 1 (27-08-2008)

Identifiants

Citer

Xavier Sauvage, Anite Dédé, Alexandra Cabello Muñoz, Bertrand Huneau. Precipitate stability and recrystallisation in the weld nuggets of friction stir welded Al-Mg-Si and Al-Mg-Sc alloys.. Materials Science and Engineering: A, 2008, 491, pp.364. ⟨10.1016/j.msea.2008.02.006⟩. ⟨hal-00314076⟩
158 Consultations
217 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More