Influence of experimental parameters on physical properties of porous silicon and oxidized porous silicon layers

Résumé

This paper reports physical properties of porous silicon and oxidized porous silicon, manufactured by anodisation from heavily p-type doped silicon wafers as a function of experimental parameters. The growth rate and refractive index of the layers were studied at different applied current densities and glycerol concentrations in electrolyte. When the current density varied from 5 to 100 mA/cm2, the refractive index was between 1.2 and 2.4 which corresponded to a porosity range from 42 to 85%. After oxidation, the porosity decreased and was between 2 and 45% for a refractive index range from 1.22 to 1.46. The thermal processing also induced an increase in thickness which was dependent on the initial porosity. This increase in thickness was more important for the lowest porosities. Lastly, the roughness of the porous layer/silicon substrate interface was studied at different applied current densities and glycerol concentrations in solution. Roughness decreased when the current density or glycerol concentration increased. Moreover, roughness was also reduced by thermal oxidation.
Fichier principal
Vignette du fichier
Charrier2007.pdf (556.74 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-00264785 , version 1 (09-11-2021)

Licence

Paternité

Identifiants

Citer

Joël Charrier, Vincent Alaiwan, Parastesh Pirasteh, Adel Najar, Michel Gadonna. Influence of experimental parameters on physical properties of porous silicon and oxidized porous silicon layers. Applied Surface Science, 2007, 253 (21), pp.8632-8636. ⟨10.1016/j.apsusc.2007.04.056⟩. ⟨hal-00264785⟩
86 Consultations
49 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More