New considerations about the fracture mode of PZT ceramics

Résumé

Sintered bulk ceramics, such as PZT are brittle materials. This macroscopically implies a statistical distribution of the ultimate strengths, because defects, such as pores or cracks are responsible for the initiation of the specimen failure. Another aspect of this fracture phenomenon is the crack propagation inside the material, along grain boundaries or through the grains themselves. An experimental study was carried out on hard and soft PZT by means of a scanning electron microscopy (SEM) quantitative analysis of tensile fractured areas. This reveals that the fracture mode is mixed, although it seems to be rather intragranular for hard ceramics and more intergranular for soft ones. Further investigations deal with the characterization of the residual porosity, which has to be distinguished from the population of critical defects. This porosity is located at grain boundaries and likely acts also as a stress concentrator and has an effect on the fracture mode and mechanical properties. For doped hard and soft PZT, a careful analysis of the microstructure is thus achieved through transmission electron microscopy (TEM) micrographs. Furthermore, domain structure is analysed for hard and soft PZT.
Fichier principal
Vignette du fichier
Guillon2005.pdf (253.61 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Licence : CC BY - Paternité

Dates et versions

hal-00019132 , version 1 (25-04-2023)

Identifiants

Citer

Olivier Guillon, Dominique Perreux, Frédéric Thiebaud, Christian Courtois, Philippe Champagne, et al.. New considerations about the fracture mode of PZT ceramics. Journal of the European Ceramic Society, 2005, 25 (12), pp.2421-2424. ⟨10.1016/j.jeurceramsoc.2005.03.074⟩. ⟨hal-00019132⟩
93 Consultations
19 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More