Crack Bridging Mechanism for Glass Strengthening by Organosilane Water-Based Coatings - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Non-Crystalline Solids Année : 2005

Crack Bridging Mechanism for Glass Strengthening by Organosilane Water-Based Coatings

Résumé

We used an epoxysilane/aminosilane coating deposited from an aqueous solution to strengthen flat glass. We studied film formation, interfacial and mechanical properties of the film. The film is highly cross-linked with a 6 GPa Young's modulus and good adhesion. Our results suggest that crack face bridging accounts for most of the 75 % reinforcement in this system.
Fichier principal
Vignette du fichier
CrackBridging.pdf (407.59 Ko) Télécharger le fichier
Loading...

Dates et versions

hal-00003078 , version 1 (14-10-2004)

Identifiants

Citer

Renaud Briard, Caroline Heitz, Etienne Barthel. Crack Bridging Mechanism for Glass Strengthening by Organosilane Water-Based Coatings. Journal of Non-Crystalline Solids, 2005, 351, pp.323-330. ⟨10.1016/j.jnoncrysol.2004.11.004⟩. ⟨hal-00003078⟩
71 Consultations
201 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More