Asymmetric Silver to Oxide Adhesion in Multilayers Deposited on Glass by Sputtering

Résumé

We have developed a wedge-loaded double-cantilever beam adhesion measurement set-up for thin films deposited on glass by sputtering. The test is described in details. Results on the Glass/sublayer/Ag/ZnO multilayer provide evidence that \SnOd\ or \TiOd\ perform better than ZnO as a sublayer. Then however, rupture within the multilayer shifts to the upper Ag/ZnO interface. The latter is shown to be tougher than the lower ZnO/Ag interface, an asymmetry due to non-equilibrium interfacial structures.
Fichier principal
Vignette du fichier
silver_adhesion_v2b.pdf (181.66 Ko) Télécharger le fichier

Dates et versions

hal-00002198 , version 1 (12-07-2004)

Identifiants

Citer

Etienne Barthel, Olivier Kerjan, Pascal Nael, Nicolas Nadaud. Asymmetric Silver to Oxide Adhesion in Multilayers Deposited on Glass by Sputtering. Thin Solid Films, 2005, 473/2, pp.272-277. ⟨hal-00002198⟩
377 Consultations
648 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More