Damage Nucleation During Transverse Creep of a Directionally Solidified Ni-based Superalloy

Résumé

A directionally solidified Ni-based superalloy DS200 is investigated under low (750 • C) and high temperature (900 • C) transverse creep. In-situ creep tests with strain measurements are performed to capture creep strain evolution in the individual crystallographic grains. Moreover, the microstructure configurations that promote damage nucleation are identified as a function of the loading condition. High angle grain boundaries are the preferred sites for crack nucleation under all investigated loading conditions. However, grain boundary configurations promoting crack nucleation are observed to significantly differ as a function of the loading conditions. Such observation is discussed in view of creep behavior and damage processes.
Fichier principal
Vignette du fichier
Preprint DS200.pdf (2.68 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03871117 , version 1 (25-11-2022)

Identifiants

Citer

Jean Charles Stinville, Lorena Mataveli Suave, Florent Mauget, Lionel Marcin, Patrick Villechaise, et al.. Damage Nucleation During Transverse Creep of a Directionally Solidified Ni-based Superalloy. Materials Science and Engineering: A, 2022, 858, pp.144089. ⟨10.1016/j.msea.2022.144089⟩. ⟨hal-03871117⟩
17 Consultations
94 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More