Investigation of the yarns sliding during the triaxial braided composite reinforcements forming
Etude des défauts de glissements lors de la mise en forme de renforts tressés triaxiales
Résumé
The composite reinforcements forming is a complicated physical stage, which concerns the complex deformability behaviours. In the present paper, the deformability of the triaxial braided fabrics as one of the advanced composite reinforcements is investigated. The yarns sliding along the longitudinal yarn direction is the primary forming behaviour during the triaxial braids forming, which is quite distinct from the woven fabrics forming. Moreover, the yarns sliding along two yarn directions present a big difference between the axial and bias yarns for the triaxial braided structures. The manufacturing defects during the triaxle braided fabrics forming such as fibre vacancies are also discussed. The influence of the yarns sliding on the forming defects and the quality of composite parts is summarized.
La mise en forme de renforts composites est une étape qui met en jeu les comportements complexes de la déformabilité du renfort et qui se doit d’être maitrisée. Dans cet article, nous étudions la déformabilité des tresses triaxiales en tant que renfort de composite. Le glissement des mèches dans la direction longitudinale des mèches est un phénomène important lors de la mise en forme des tresses triaxiales, dont la déformabilité est très différente de celle des renforts tissés. De plus, le glissement des mèches dans les deux directions, axiales et de biais pour la structure tresse triaxiale se doit d’être analysée. Les défauts de fabrication pendant la mise en forme des tresses triaxiales, comme par exemple le manque de fibres, sont également abordés. L'influence du glissement de mèche sur les défauts de la mise en forme et la qualité des pièces composites est étudiée.
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|
Loading...