Suspended core tellurite glass optical fibers for infrared supercontinuum generation - Laboratoire Interdisciplinaire Carnot de Bourgogne Accéder directement au contenu
Article Dans Une Revue Optical Materials Année : 2011

Suspended core tellurite glass optical fibers for infrared supercontinuum generation

Julien Fatome
Johann Troles
G. Renversez

Résumé

We report the fabrication and characterization of tellurite TeO(2)-ZnO-Na(2)O (TZN) microstructured suspended core optical fibers (MOFs). These fibers are designed for infrared supercontinuum generation with zero dispersion wavelength (ZDW) at 1.451 mu m. The measured losses at this wavelength are approximately 6 dB/m for a MOF with a 2.2 mu m diameter core. The effective area of a particular fiber is 3.5 mu m(2) and the nonlinear coefficient is calculated to be 437 W(-1)km(-1). By pumping a 20 cm long fiber at 1.56 mu m with a sub-nj femtosecond laser source, we generate a supercontinuum (SC) spanning over 800 nm in the 1-2 mu m wavelength range.
Fichier principal
Vignette du fichier
Savelii2011.pdf (468.75 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-00655170 , version 1 (21-04-2021)

Licence

Paternité

Identifiants

Citer

I. Savelii, J.C. Jules, G. Gadret, B. Kibler, Julien Fatome, et al.. Suspended core tellurite glass optical fibers for infrared supercontinuum generation. Optical Materials, 2011, 33 (11), pp.1661-1666. ⟨10.1016/j.optmat.2011.05.010⟩. ⟨hal-00655170⟩
544 Consultations
122 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More