Workability tests on fresh concrete formulated with eco-friendly admixture

Résumé

Extra-cellular compounds, secreted by microorganisms into their surroundings, can be integrated in concrete composition as admixtures. These substances are important in biofilm formation and some of them can be used as corrosion inhibitor of concrete reinforcement. This paper deals with products made with polymeric biological compounds allowing the development of more eco-friendly concrete. The influence of this environmentally friendly bio admixture on setting time, workability, bending and compressive strengths of various mortar based materials made of CEM I, CEM III and CEM V was studied. Mechanical tests were carried out to highlight the influence of admixture in workability and hardening of samples containing the biological product with ratio in the range of 0 - 2.5%. It was demonstrated that the presence of the new bio-polymeric admixture in mortar decreases their compressive strength after 28 days of standard curing, in spite of remaining higher than standard minimal strength. Furthermore, Vicat needle experiments have shown a tendency of this admixture to decrease the setting time. A discussion was fmally proposed in order to correlate the setting times and the decrease of the mortar compressive strength, corresponding in fact to a hardening delay.
Fichier non déposé

Dates et versions

hal-02948889 , version 1 (25-09-2020)

Identifiants

  • HAL Id : hal-02948889 , version 1
  • WOS : 000392048800019

Citer

Nicolas Serres, Huan He, Sébastien Roux, Thierry Meylheuc, Francoise Feugeas. Workability tests on fresh concrete formulated with eco-friendly admixture. 7th Asian Symposium on Polymers in Concrete (ASPIC 2012), Oct 2012, Istanbul, Turkey. ⟨hal-02948889⟩
17 Consultations
0 Téléchargements

Partager

Gmail Facebook X LinkedIn More