Liquid metal embrittlement susceptibility of T91 steel by Lead-Bismuth

Résumé

Previous studies on T91 steel in its standard metallurgical state found no evidence for Liquid Metal Embrittlement (LME) by eutectic Pb-Bi. In this paper, we report clear evidence that this steel can be embrittled by Pb-Bi when direct contact between the steel and the liquid metal is obtained by prior ion beam sputtering.
Fichier principal
Vignette du fichier
LME-T91ScriptaMet.pdf (889.1 Ko) Télécharger le fichier
Loading...

Dates et versions

hal-00000806 , version 1 (03-11-2003)
hal-00000806 , version 2 (09-07-2004)

Identifiants

  • HAL Id : hal-00000806 , version 2

Citer

Thierry Auger, Gérard Lorang. Liquid metal embrittlement susceptibility of T91 steel by Lead-Bismuth. 2004. ⟨hal-00000806v2⟩
52 Consultations
467 Téléchargements

Partager

Gmail Facebook X LinkedIn More